Knife Making Steel bar, 1084 Carbon Steel in 3.5 x 38-40 x 1000 mm
The most popular carbon steel for new makers is probably 1084 Carbon Steel, due to ease of heat treatment. High quality blade steel for knife making by forging and stock removal. Suitable for use by hand tools as well as grinder.
The blade can be heat treated any way you can get it hot enough, no soak time or complicated temperature changes required.
For instance with a forge, a blowtorch or a kiln heating the blade until dull orange and checked against a magnet.
When the steel no longer is attracted to the magnet, it has hit critical temperature and can be QUICKLY quenched in canola oil.
Size of steel bar is about 3.5 mm thick, 38-41 mm wide and 1000 mm long. Note they are cut from plate and vary from 38 to 41 mm in width.
The steel comes already annealed and ready to work.
Annealed means the steel is "soft" and workable with hand tools.
It can be drilled, filed, ground and shaped with relative ease. Look up hand filing jig on youtube for an easy to make hand filing jig for making even bevels.
This steel will need to be heat treated, either at home or by sending it away for professional heat treatment.
Heat treating 1084 Carbon Steel:
- Heat steel to non-magnetic (about 815-820 C)
- No hold time, quench as soon as hot enough
- Quench in 30-40 C canola oil for a fast, effective quench
- Temper twice, for 2 hours at 200 C (in a kitchen stove, for instance)
Optional: it is recommended to stress relieve the steel by heating it to red hot and letting it air cool a couple of times before quenching. This helps reduce stress in the steel before the (stressful) quench. If wanting to normalise to refine grain size, heat to 870 C and let air cool 2-3 times. Normalising is done if the steel has been forged, if doing stock removal this step is not usually done.
showing blades after normalizing cycles, where the blades are heated and left to air cool. This is often done before quenching, helping to releave tension from the blade before quenching. It also helps reduce the grain size if the blade has been overheated and is generally a good idea.
Great product, easy to use.
Happy with the steel so far. Came with a bit of a bend but probably due to transport. Hope it becomes a few lovely pieces of work.
Very happy with this product fast delivery
Straightest lot I've gotten, very nice steel to work with
1. It's perfectly workable for hand cutting and filing (and hand sanding...ugh..)
2. Easy to heat treat using non professional equipment in DIY forge
3. The 36-40mm steel width is much appreciated to make curved blades and full tangs
4. As this was my first purchase, not sure yet how well the steel will hold its edge.
5. The sales and after- purchase service from Bjorn is outstanding.
6. These are good, honest people to deal with.
Spot on, as requested. Communication and delivery was great. I'll definitely deal with this company again.
Very impressed with how easy it was to work with, and after heat treat was shocked at how much harder it was to work
I have made several blades with this steel from Nordic Edge. Even as a newbie maker with a home -made coal forge, it is easy to work, heats evenly and quenches well. Holds a wicked edge and has withstood being thrown on the ground (just out of curiosity ;) after tempering in a home oven. Price is good too.
All the products I've ordered from Creativeman have been top quality, steel file guides and jigs etc. Keep up the great work . Thanks Brian